Chemical Treated Film

Product Name：Chemical Treated Film
Type：RD103
Typical Properties：
1. Surface of film after chemical treatment, high adhesion between film and aluminum layer, Peel Strength can be above 4N/15mm
2. For high adhension of aluminum layer, increase the thickness of Aluminum layer and no Aluminum Layer peels, to extend the contents of the shelf-life, and the fragrance of good
3. By increasing the thickness of Aluminum layer so that it will have a higher barrier
4. Good water resistance
5. Good high temperature resistance

Specification：

Thickness of Film	Thickness of Aluminum layer	Width	Roll Diameter	Paper core ID
12-36μm	300-700A	≤2100mm	≤780mm	76mm(3″),152mm(6″)
Regular Specification：12μm，Thickness of Aluminum layer is 380A、500A，Length: 4000m、6000m、8000m/roll，3″ paper core, other specifications are customized.

Typical Properties：

Item		Units	Typical Values	Testing Methods
Thickness of Film		μm	12	ASTM D-374
Tensile Strength	MD	Mpa	212	ASTM D-882
Tensile Strength	TD	Mpa	222	ASTM D-882
Elongation At Break	MD	%	132	ASTM D-882
Elongation At Break	TD	%	125	ASTM D-882
Shrinkage(150℃，30min）	MD	%	1.4	ASTM D-1204
Shrinkage(150℃，30min）	TD	%	0.3	ASTM D-1204
Wetting Tension	Metal side	mN/m	54	ASTM D-2578
Friction coefficient(base film)		——	0.3	ASTM D-1894
Haze		%	3.2	ASTM D-1003
Glossness		%	131	ASTM D-2457
Thickness of Aluminum layer		A	500
		Ω/□	1.02	GB/T 15717
		O.D	2.52	X·Rite361
		(Light Transmission)VLT		ASTM D1746
Uniformity of Aluminum Layer		%	5	GB/T 15717
Adhesion of Alumunium Layer		%	No Aluminum Layer Peels	3M Tape
WTR(38℃,90%RH)		g/m2·24hr	0.42	ASTM E96
VOTR(23℃,0%RH)		cm3/m2·1atm·24hr	0.88	ASTM D1434
Peel Strength		N/25mm	7.2

Applications：
Composite structure can arrive at 3-Ply, and can be used 2-ply in place of 3-ply, thereby reducing costs; suitable for milk, coffee, cosmetics, jellies, wines, drinks, pesticides and snacks packaging various solid and liquid high-grade packaging, can extend the shelf life of contents, and a good fragrance; can replace part of the packaging foil composite structure; used for higher water resistance of the occasion, and for liquid packaging improved; can be used in pasteurized